STL003F is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL003B
STL003B is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL002F
STL002F is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL002B
STL002B is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL001P
STL001P is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL001F
STL001F is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL001GP
STL001GP is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
STL001B
STL001B is polyethylene-based material used as tie layers with good adhesion to EVOH and Aluminum. The presence of the grafted anhydride groups allow to attach itself covalently to the surface of the barrier layer due to the polar groups present on it. This results in increased interfacial adhesive strength and process ability.
MEHI100
MEHI100 is low density polyethylene filled with 80% calcium carbonate. This masterbatch improves processability and dimensional stability and reduces the price of the final product. It suitable for film blowing, blow molding and injection molded parts applications.
MES100
MES100 is high density polyethylene filled with 80% calcium carbonate. This masterbatch improves processability and dimensional stability and reduces the price of the final product. It suitable for film blowing, blow molding and injection molded parts applications.
MEF100
MEF100 is low density polyethylene filled with 80% calcium carbonate. This masterbatch improves processability and dimensional stability and reduces the price of the final product. It suitable for film blowing and blow molding applications.